FORMODAL BM-6082 Walzplatte

EN AW-6082

circular - machined surface

A technical illustration of the product with dimensions of the material FORMODAL BM-6082 Walzplatte from the material Aluminum in the shape circular - machined surface
  • Form circular - machined surface
  • Material Aluminum
  • Material EN AW-6082
  • Material chemically EN 573-3 Al Si1 Mg Mn
  • DIN 3.2315

No product available for your selection.

You can find an overview of all standard dimensions here in our stock list.
Request drawing part
An image of the material EN AW-6082 from the material Aluminum in the shape circular - machined surface
A technical illustration of the product of the material EN AW-6082 from the material Aluminum in the shape circular - machined surface

Areas of application

Shipbuilding

Railed vehicles

 Boiler and container construction

Areas of application

Aerospace

Military technology



Features of this material

  •  Good corrosion resistance
  • Good welding properties
  • Curable alloy

Features of this material

  • Good machinability 

Information about the material

  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.25
    Cu (to) 0.1
    Fe (to) 0.5
    Mg (from) 0.6
    Mg (to) 1.2
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.7
    Si (to) 1.3
    Ti (to) 0.1
    Total 0,15
    Zn (to) 0.2

    (a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.

  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 1
  • Corrosion resistance
    Normal atmosphere 1
    Seawater atmosphere 2
  • Food industry
    suitable according to DIN EN 602 Yes
  • Forming
    Bending 3
    Bending delivery conditions T3 · T4
    Deep drawing (conditional) 2
    Deep drawing conditions O
    Drop forging 2
    Extruding 2
    Impact extrusion 2
    Impact extrusion conditions O
    Open die forging 2
    Press 2
    Press conditions O
    Upsetting (Conditional) 2
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions ≤ 30°C/h up to 250°C, below 250°C
    in the air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 4 h
    Heating temperature max. 190 °C
    Heating temperature min. 155 °C
    Quenching Water, Air
    Solution annealing max. 540 °C
    Solution annealing min. 525 °C
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 2
    soft annealed 4
  • Material
    Colorcode Enzianblau (RAL 5010)
    Material chemically EN 573-3 Al Si1 Mg Mn
    DIN 3.2315
    DIN (old designation) Al Mg Si1
    France AFNOR A-SGM0,7
    Italy UNI 9006/4
    Norway -
    Spain L-3453
    Sweden 144,212
    United Kingdom BS H30
    Shape specific material FORMODAL BM-6082 Walzplatte
  • Mechanical surface treatment
    Polishing 1
  • Organic coating
    Painting / Coating 2
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Density 2.7 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 70 GPa
    Shear modulus 26.4 GPa
    Specific heat 896 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 4
    Brazing with flux 3
    Friction soldering 2
    Soft soldering with flux 3
  • Welding
    Gas 3
    MIG 1
    Resistance spot welding 3
    TIG 2
    welding additives

    • SG-Al Mg4
    • SG-Al Mg4,5 Mn
    • SG-Al Si5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.25
    Cu (to) 0.1
    Fe (to) 0.5
    Mg (from) 0.6
    Mg (to) 1.2
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.7
    Si (to) 1.3
    Ti (to) 0.1
    Total 0,15
    Zn (to) 0.2

    (a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.

  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 1
  • Corrosion resistance
    Normal atmosphere 1
    Seawater atmosphere 2
  • Food industry
    suitable according to DIN EN 602 Yes
  • Forming
    Bending 3
    Bending delivery conditions T3 · T4
    Deep drawing (conditional) 2
    Deep drawing conditions O
    Drop forging 2
    Extruding 2
    Impact extrusion 2
    Impact extrusion conditions O
    Open die forging 2
    Press 2
    Press conditions O
    Upsetting (Conditional) 2
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions ≤ 30°C/h up to 250°C, below 250°C
    in the air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 4 h
    Heating temperature max. 190 °C
    Heating temperature min. 155 °C
    Quenching Water, Air
    Solution annealing max. 540 °C
    Solution annealing min. 525 °C
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 2
    soft annealed 4
  • Material
    Colorcode Enzianblau (RAL 5010)
    Material chemically EN 573-3 Al Si1 Mg Mn
    DIN 3.2315
    DIN (old designation) Al Mg Si1
    France AFNOR A-SGM0,7
    Italy UNI 9006/4
    Norway -
    Spain L-3453
    Sweden 144,212
    United Kingdom BS H30
    Shape specific material FORMODAL BM-6082 Walzplatte
  • Mechanical surface treatment
    Polishing 1
  • Organic coating
    Painting / Coating 2
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Density 2.7 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 70 GPa
    Shear modulus 26.4 GPa
    Specific heat 896 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 4
    Brazing with flux 3
    Friction soldering 2
    Soft soldering with flux 3
  • Welding
    Gas 3
    MIG 1
    Resistance spot welding 3
    TIG 2
    welding additives

    • SG-Al Mg4
    • SG-Al Mg4,5 Mn
    • SG-Al Si5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.25
    Cu (to) 0.1
    Fe (to) 0.5
    Mg (from) 0.6
    Mg (to) 1.2
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.7
    Si (to) 1.3
    Ti (to) 0.1
    Total 0,15
    Zn (to) 0.2

    (a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.

  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 1
  • Corrosion resistance
    Normal atmosphere 1
    Seawater atmosphere 2
  • Food industry
    suitable according to DIN EN 602 Yes
  • Forming
    Bending 3
    Bending delivery conditions T3 · T4
    Deep drawing (conditional) 2
    Deep drawing conditions O
    Drop forging 2
    Extruding 2
    Impact extrusion 2
    Impact extrusion conditions O
    Open die forging 2
    Press 2
    Press conditions O
    Upsetting (Conditional) 2
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions ≤ 30°C/h up to 250°C, below 250°C
    in the air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 4 h
    Heating temperature max. 190 °C
    Heating temperature min. 155 °C
    Quenching Water, Air
    Solution annealing max. 540 °C
    Solution annealing min. 525 °C
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 2
    soft annealed 4
  • Material
    Colorcode Enzianblau (RAL 5010)
    Material chemically EN 573-3 Al Si1 Mg Mn
    DIN 3.2315
    DIN (old designation) Al Mg Si1
    France AFNOR A-SGM0,7
    Italy UNI 9006/4
    Norway -
    Spain L-3453
    Sweden 144,212
    United Kingdom BS H30
    Shape specific material FORMODAL BM-6082 Walzplatte
  • Mechanical surface treatment
    Polishing 1
  • Organic coating
    Painting / Coating 2
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Density 2.7 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 70 GPa
    Shear modulus 26.4 GPa
    Specific heat 896 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 4
    Brazing with flux 3
    Friction soldering 2
    Soft soldering with flux 3
  • Welding
    Gas 3
    MIG 1
    Resistance spot welding 3
    TIG 2
    welding additives

    • SG-Al Mg4
    • SG-Al Mg4,5 Mn
    • SG-Al Si5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.25
    Cu (to) 0.1
    Fe (to) 0.5
    Mg (from) 0.6
    Mg (to) 1.2
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.7
    Si (to) 1.3
    Ti (to) 0.1
    Total 0,15
    Zn (to) 0.2

    (a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.

  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 1
  • Corrosion resistance
    Normal atmosphere 1
    Seawater atmosphere 2
  • Food industry
    suitable according to DIN EN 602 Yes
  • Forming
    Bending 3
    Bending delivery conditions T3 · T4
    Deep drawing (conditional) 2
    Deep drawing conditions O
    Drop forging 2
    Extruding 2
    Impact extrusion 2
    Impact extrusion conditions O
    Open die forging 2
    Press 2
    Press conditions O
    Upsetting (Conditional) 2
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions ≤ 30°C/h up to 250°C, below 250°C
    in the air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 4 h
    Heating temperature max. 190 °C
    Heating temperature min. 155 °C
    Quenching Water, Air
    Solution annealing max. 540 °C
    Solution annealing min. 525 °C
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 2
    soft annealed 4
  • Material
    Colorcode Enzianblau (RAL 5010)
    Material chemically EN 573-3 Al Si1 Mg Mn
    DIN 3.2315
    DIN (old designation) Al Mg Si1
    France AFNOR A-SGM0,7
    Italy UNI 9006/4
    Norway -
    Spain L-3453
    Sweden 144,212
    United Kingdom BS H30
    Shape specific material FORMODAL BM-6082 Walzplatte
  • Mechanical surface treatment
    Polishing 1
  • Organic coating
    Painting / Coating 2
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Density 2.7 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 70 GPa
    Shear modulus 26.4 GPa
    Specific heat 896 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 4
    Brazing with flux 3
    Friction soldering 2
    Soft soldering with flux 3
  • Welding
    Gas 3
    MIG 1
    Resistance spot welding 3
    TIG 2
    welding additives

    • SG-Al Mg4
    • SG-Al Mg4,5 Mn
    • SG-Al Si5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.25
    Cu (to) 0.1
    Fe (to) 0.5
    Mg (from) 0.6
    Mg (to) 1.2
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.7
    Si (to) 1.3
    Ti (to) 0.1
    Total 0,15
    Zn (to) 0.2

    (a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.

  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 1
  • Corrosion resistance
    Normal atmosphere 1
    Seawater atmosphere 2
  • Food industry
    suitable according to DIN EN 602 Yes
  • Forming
    Bending 3
    Bending delivery conditions T3 · T4
    Deep drawing (conditional) 2
    Deep drawing conditions O
    Drop forging 2
    Extruding 2
    Impact extrusion 2
    Impact extrusion conditions O
    Open die forging 2
    Press 2
    Press conditions O
    Upsetting (Conditional) 2
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions ≤ 30°C/h up to 250°C, below 250°C
    in the air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 4 h
    Heating temperature max. 190 °C
    Heating temperature min. 155 °C
    Quenching Water, Air
    Solution annealing max. 540 °C
    Solution annealing min. 525 °C
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 2
    soft annealed 4
  • Material
    Colorcode Enzianblau (RAL 5010)
    Material chemically EN 573-3 Al Si1 Mg Mn
    DIN 3.2315
    DIN (old designation) Al Mg Si1
    France AFNOR A-SGM0,7
    Italy UNI 9006/4
    Norway -
    Spain L-3453
    Sweden 144,212
    United Kingdom BS H30
    Shape specific material FORMODAL BM-6082 Walzplatte
  • Mechanical surface treatment
    Polishing 1
  • Organic coating
    Painting / Coating 2
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Density 2.7 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 70 GPa
    Shear modulus 26.4 GPa
    Specific heat 896 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 4
    Brazing with flux 3
    Friction soldering 2
    Soft soldering with flux 3
  • Welding
    Gas 3
    MIG 1
    Resistance spot welding 3
    TIG 2
    welding additives

    • SG-Al Mg4
    • SG-Al Mg4,5 Mn
    • SG-Al Si5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.25
    Cu (to) 0.1
    Fe (to) 0.5
    Mg (from) 0.6
    Mg (to) 1.2
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.7
    Si (to) 1.3
    Ti (to) 0.1
    Total 0,15
    Zn (to) 0.2

    (a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.

  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 1
  • Corrosion resistance
    Normal atmosphere 1
    Seawater atmosphere 2
  • Food industry
    suitable according to DIN EN 602 Yes
  • Forming
    Bending 3
    Bending delivery conditions T3 · T4
    Deep drawing (conditional) 2
    Deep drawing conditions O
    Drop forging 2
    Extruding 2
    Impact extrusion 2
    Impact extrusion conditions O
    Open die forging 2
    Press 2
    Press conditions O
    Upsetting (Conditional) 2
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions ≤ 30°C/h up to 250°C, below 250°C
    in the air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 4 h
    Heating temperature max. 190 °C
    Heating temperature min. 155 °C
    Quenching Water, Air
    Solution annealing max. 540 °C
    Solution annealing min. 525 °C
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 2
    soft annealed 4
  • Material
    Colorcode Enzianblau (RAL 5010)
    Material chemically EN 573-3 Al Si1 Mg Mn
    DIN 3.2315
    DIN (old designation) Al Mg Si1
    France AFNOR A-SGM0,7
    Italy UNI 9006/4
    Norway -
    Spain L-3453
    Sweden 144,212
    United Kingdom BS H30
    Shape specific material FORMODAL BM-6082 Walzplatte
  • Mechanical surface treatment
    Polishing 1
  • Organic coating
    Painting / Coating 2
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Density 2.7 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 70 GPa
    Shear modulus 26.4 GPa
    Specific heat 896 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 4
    Brazing with flux 3
    Friction soldering 2
    Soft soldering with flux 3
  • Welding
    Gas 3
    MIG 1
    Resistance spot welding 3
    TIG 2
    welding additives

    • SG-Al Mg4
    • SG-Al Mg4,5 Mn
    • SG-Al Si5

1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified

More questions about BIKAR?

Information about BIKAR, our product range and our service can be found here:

ABOUT OUR COMPANY