EN AW-7075
tube - round as bar
- Form tube - round as bar
- Material Aluminum
- Material EN AW-7075
- Material chemically EN 573-3 Al Zn5,5 Mg Cu
- DIN 3.4365
![An image of the material EN AW-7075 from the material Aluminum in the shape tube - round as bar](https://my.bikar.com/media/cache/sylius_shop_product_detail_mainimage_thumbnail/a6/bd/b9fc9a393c02dc27bc57c835e6b8.jpg)
![A technical illustration of the product of the material EN AW-7075 from the material Aluminum in the shape tube - round as bar](https://my.bikar.com/media/cache/sylius_shop_product_detail_media_medium_thumbnail/60/d4/545c7d19e4f6462532b4c7ff02dc.jpg)
BIKAR Metals companies
Tool making, mould making and model making
Aerospace
Military technology
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
Aviation | Yes |
Cr (from) | 0.18 |
Cr (to) | 0.28 |
Cu (from) | 1.2 |
Cu (to) | 2 |
Fe (from) | 0.5 |
Mg (from) | 2.1 |
Mg (to) | 2.9 |
Mn (to) | 0.3 |
Other | 0,05 |
Rest | Aluminium |
Si (to) | 0.4 |
Ti (to) | 0.2 |
Total | 0,15 |
Zn (from) | 5.1 |
Zn (to) | 6.1 |
Anodise - decorative | 5 |
Anodising - protective anodising | 3 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
suitable according to DIN EN 602 | No |
Bending | 4 |
Bending delivery conditions | O |
Deep drawing (conditional) | 4.5 |
Deep drawing conditions | O |
Drop forging | 4 |
Extruding | 4.5 |
Impact extrusion | 5 |
Open die forging | 4 |
Press | 5 |
Upsetting (Conditional) | 5 |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
≤ 30°C/h to 230°C + 3 – 5 hours hold time, below 230°C in air |
Cold ageing condition | anschließend warmauslagern |
Cold ageing max. | 5 d |
Cold ageing min. | 3 d |
Heat ageing max. | 24 h |
Heat ageing min. | 12 h |
Heating temperature max. | 125 °C |
Heating temperature min. | 110 °C |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 480 °C |
Solution annealing min. | 470 °C |
dimensional stability | 4.5 |
Eroding | 1 |
hardened | 2 |
Colorcode | Blaulila (RAL 4005) |
Material chemically EN 573-3 | Al Zn5,5 Mg Cu |
DIN | 3.4365 |
DIN (old designation) | Al Zn Mg Cu1,5 |
France AFNOR | A-Z5GU |
Italy UNI | 9007/2 |
United Kingdom BS | 2L95 |
Polishing | 1 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24.3 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.6 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 72 GPa |
Shear modulus | 27.1 GPa |
Specific heat | 862 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 5 |
Soft soldering with flux | 5 |
Gas | 5 |
MIG | 5 |
Resistance spot welding | 2 |
TIG | 5 |
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified