Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
-
Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
-
Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
-
Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
-
Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
-
Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
-
Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
-
Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
-
Aviation
-
Chemical specifications
Be (from)
|
0
|
Be (to)
|
0
|
Co (from)
|
0
|
Co (to)
|
0
|
Cr (to)
|
0,1
|
Cu (to)
|
0,1
|
Fe (to)
|
0,35
|
Mg (from)
|
0,45
|
Mg (to)
|
0,9
|
Mn (to)
|
0,1
|
Other
|
max. 0,05
|
Rest
|
Al
|
Si (from)
|
0,2
|
Si (to)
|
0,6
|
Ti (to)
|
0,1
|
Total
|
max. 0,15 a) b)
|
Zn (to)
|
0,1
|
-
Corrosion resistance
Normal atmosphere
|
1,5
|
Seawater atmosphere
|
2
|
-
Cutting
Laser cutting
|
3
|
Plasma cutting
|
2
|
Sawing
|
2
|
Shear cutting
|
2
|
Waterjet cutting
|
1
|
-
Food industry
suitable according to DIN EN 602
|
No
|
-
Forming
Bending
|
5
|
Bending delivery conditions
|
T6
|
Extruding
|
2
|
Press
|
5
|
Press conditions
|
T6
|
Upsetting (Conditional)
|
5
|
Upsetting conditions
|
T6
|
-
Heat treatment - Softannealing
Heating time max.
|
2 h
|
Heating time min.
|
1 h
|
Annealing temperature max.
|
420 °C
|
Annealing temperature min.
|
380 °C
|
-
Heat treatment - Solution annealing
Cold ageing condition
|
danach
|
Cold ageing max.
|
8 d
|
Cold ageing min.
|
5 d
|
Heat ageing max.
|
16 h
|
Heat ageing min.
|
4 h
|
Heating temperature max.
|
190 °C
|
Heating temperature min.
|
155 °C
|
Solution annealing max.
|
540 °C
|
Solution annealing min.
|
525 °C
|
-
Material
Material chemically EN 573-3
|
Aluminium Al Mg0.7 Si
|
DIN
|
3,2306
|
DIN (old designation)
|
AlMgSi
|
Italy UNI
|
[P-AlSi0,4Mg]
|
Spain
|
L-3441 [Al-0,7MgSi]
|
Sweden
|
144.104
|
United Kingdom BS
|
BS-H9
|
-
physical properties
Coefficient of thermal expansion from 20 to 100°C
|
23.4 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 200°C
|
24.5 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from 20 to 300°C
|
25.6 K⁻¹10⁻⁶
|
Coefficient of thermal expansion from -50 to 20°C
|
21.8 K⁻¹10⁻⁶
|
Density
|
2.7 g/cm³
|
Specific heat
|
900 J/(kg·K)
|
Thermal conductivity max.
|
200 W/m*K
|
-
Soldering
Brazing
|
3
|
Brazing with flux
|
3
|
Soft soldering
|
3
|
Soft soldering with flux
|
3
|
-
Welding
Friction stir welding
|
2
|
Friction welding
|
2
|
Laser
|
2
|
MIG
|
2
|
Plasma
|
2
|
Resistance spot welding
|
3
|
TIG
|
2
|
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified