CW453K
flat bar
- Form flat bar
- Material Bronze
- Material CW453K
- Material chemically EN 573-3 Bronze Cu Sn 8
BIKAR Metals companies
apparatus parts and wire cloth for the paper and chemical industry
pump parts
highly stressed worms, gear wheels, bolts and screws
plain bearings and slideways
Aviation | No |
Fe (from) | 0.1 |
Fe (to) | 0.1 |
Ni (from) | 0.2 |
Ni (to) | 0.2 |
Other | 0.2 |
P (from) | 0.01 |
P (to) | 0.4 |
Pb (from) | 0.02 |
Pb (to) | 0.02 |
Rest | Cu |
Sn (from) | 7.5 |
Sn (to) | 8.5 |
Zn (from) | 0.2 |
Zn (to) | 0.2 |
suitable according to DIN EN 602 | No |
Material chemically EN 573-3 | Bronze Cu Sn 8 |
Material no | CW453K (2.1030) |
Coefficient of thermal expansion from 20 to 300°C | 18.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 400°C | 18.7 K⁻¹10⁻⁶ |
Density | 8.79 g/cm³ |
Modulus of elasticity at 100°C | 106 GPa |
Modulus of elasticity at 20°C | 109 GPa |
Modulus of elasticity at 200°C | 102 GPa |
Modulus of elasticity at 300°C | 98 GPa |
Modulus of elasticity at 400°C | 93 GPa |
Specific electrical conductivity at 20°C | 7.5 m/Ω*mm² |
Specific electrical conductivity at 200°C | 6.5 m/Ω*mm² |
Specific electrical resistance at 20°C | 0.133 Ω*mm²/m |
Specific electrical resistance at 200°C | 6.5 Ω*mm²/m |
Specific heat at 20°C | 0.377 J/(kg·K) |
Thermal conductivity at 20°C | 67 W/m*K |
Thermal conductivity at 200°C | 81 W/m*K |
Brazing | 1 |
Soft soldering | 1 |
Gas | 3 |
MIG | 2 |
Resistance spot welding | 2 |
TIG | 2 |
Aviation | No |
Fe (from) | 0.1 |
Fe (to) | 0.1 |
Ni (from) | 0.2 |
Ni (to) | 0.2 |
Other | 0.2 |
P (from) | 0.01 |
P (to) | 0.4 |
Pb (from) | 0.02 |
Pb (to) | 0.02 |
Rest | Cu |
Sn (from) | 7.5 |
Sn (to) | 8.5 |
Zn (from) | 0.2 |
Zn (to) | 0.2 |
suitable according to DIN EN 602 | No |
Material chemically EN 573-3 | Bronze Cu Sn 8 |
Material no | CW453K (2.1030) |
Coefficient of thermal expansion from 20 to 300°C | 18.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 400°C | 18.7 K⁻¹10⁻⁶ |
Density | 8.79 g/cm³ |
Modulus of elasticity at 100°C | 106 GPa |
Modulus of elasticity at 20°C | 109 GPa |
Modulus of elasticity at 200°C | 102 GPa |
Modulus of elasticity at 300°C | 98 GPa |
Modulus of elasticity at 400°C | 93 GPa |
Specific electrical conductivity at 20°C | 7.5 m/Ω*mm² |
Specific electrical conductivity at 200°C | 6.5 m/Ω*mm² |
Specific electrical resistance at 20°C | 0.133 Ω*mm²/m |
Specific electrical resistance at 200°C | 6.5 Ω*mm²/m |
Specific heat at 20°C | 0.377 J/(kg·K) |
Thermal conductivity at 20°C | 67 W/m*K |
Thermal conductivity at 200°C | 81 W/m*K |
Brazing | 1 |
Soft soldering | 1 |
Gas | 3 |
MIG | 2 |
Resistance spot welding | 2 |
TIG | 2 |
Aviation | No |
Fe (from) | 0.1 |
Fe (to) | 0.1 |
Ni (from) | 0.2 |
Ni (to) | 0.2 |
Other | 0.2 |
P (from) | 0.01 |
P (to) | 0.4 |
Pb (from) | 0.02 |
Pb (to) | 0.02 |
Rest | Cu |
Sn (from) | 7.5 |
Sn (to) | 8.5 |
Zn (from) | 0.2 |
Zn (to) | 0.2 |
suitable according to DIN EN 602 | No |
Material chemically EN 573-3 | Bronze Cu Sn 8 |
Material no | CW453K (2.1030) |
Coefficient of thermal expansion from 20 to 300°C | 18.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 400°C | 18.7 K⁻¹10⁻⁶ |
Density | 8.79 g/cm³ |
Modulus of elasticity at 100°C | 106 GPa |
Modulus of elasticity at 20°C | 109 GPa |
Modulus of elasticity at 200°C | 102 GPa |
Modulus of elasticity at 300°C | 98 GPa |
Modulus of elasticity at 400°C | 93 GPa |
Specific electrical conductivity at 20°C | 7.5 m/Ω*mm² |
Specific electrical conductivity at 200°C | 6.5 m/Ω*mm² |
Specific electrical resistance at 20°C | 0.133 Ω*mm²/m |
Specific electrical resistance at 200°C | 6.5 Ω*mm²/m |
Specific heat at 20°C | 0.377 J/(kg·K) |
Thermal conductivity at 20°C | 67 W/m*K |
Thermal conductivity at 200°C | 81 W/m*K |
Brazing | 1 |
Soft soldering | 1 |
Gas | 3 |
MIG | 2 |
Resistance spot welding | 2 |
TIG | 2 |
Aviation | No |
Fe (from) | 0.1 |
Fe (to) | 0.1 |
Ni (from) | 0.2 |
Ni (to) | 0.2 |
Other | 0.2 |
P (from) | 0.01 |
P (to) | 0.4 |
Pb (from) | 0.02 |
Pb (to) | 0.02 |
Rest | Cu |
Sn (from) | 7.5 |
Sn (to) | 8.5 |
Zn (from) | 0.2 |
Zn (to) | 0.2 |
suitable according to DIN EN 602 | No |
Material chemically EN 573-3 | Bronze Cu Sn 8 |
Material no | CW453K (2.1030) |
Coefficient of thermal expansion from 20 to 300°C | 18.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 400°C | 18.7 K⁻¹10⁻⁶ |
Density | 8.79 g/cm³ |
Modulus of elasticity at 100°C | 106 GPa |
Modulus of elasticity at 20°C | 109 GPa |
Modulus of elasticity at 200°C | 102 GPa |
Modulus of elasticity at 300°C | 98 GPa |
Modulus of elasticity at 400°C | 93 GPa |
Specific electrical conductivity at 20°C | 7.5 m/Ω*mm² |
Specific electrical conductivity at 200°C | 6.5 m/Ω*mm² |
Specific electrical resistance at 20°C | 0.133 Ω*mm²/m |
Specific electrical resistance at 200°C | 6.5 Ω*mm²/m |
Specific heat at 20°C | 0.377 J/(kg·K) |
Thermal conductivity at 20°C | 67 W/m*K |
Thermal conductivity at 200°C | 81 W/m*K |
Brazing | 1 |
Soft soldering | 1 |
Gas | 3 |
MIG | 2 |
Resistance spot welding | 2 |
TIG | 2 |
Aviation | No |
Fe (from) | 0.1 |
Fe (to) | 0.1 |
Ni (from) | 0.2 |
Ni (to) | 0.2 |
Other | 0.2 |
P (from) | 0.01 |
P (to) | 0.4 |
Pb (from) | 0.02 |
Pb (to) | 0.02 |
Rest | Cu |
Sn (from) | 7.5 |
Sn (to) | 8.5 |
Zn (from) | 0.2 |
Zn (to) | 0.2 |
suitable according to DIN EN 602 | No |
Material chemically EN 573-3 | Bronze Cu Sn 8 |
Material no | CW453K (2.1030) |
Coefficient of thermal expansion from 20 to 300°C | 18.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 400°C | 18.7 K⁻¹10⁻⁶ |
Density | 8.79 g/cm³ |
Modulus of elasticity at 100°C | 106 GPa |
Modulus of elasticity at 20°C | 109 GPa |
Modulus of elasticity at 200°C | 102 GPa |
Modulus of elasticity at 300°C | 98 GPa |
Modulus of elasticity at 400°C | 93 GPa |
Specific electrical conductivity at 20°C | 7.5 m/Ω*mm² |
Specific electrical conductivity at 200°C | 6.5 m/Ω*mm² |
Specific electrical resistance at 20°C | 0.133 Ω*mm²/m |
Specific electrical resistance at 200°C | 6.5 Ω*mm²/m |
Specific heat at 20°C | 0.377 J/(kg·K) |
Thermal conductivity at 20°C | 67 W/m*K |
Thermal conductivity at 200°C | 81 W/m*K |
Brazing | 1 |
Soft soldering | 1 |
Gas | 3 |
MIG | 2 |
Resistance spot welding | 2 |
TIG | 2 |
Aviation | No |
Fe (from) | 0.1 |
Fe (to) | 0.1 |
Ni (from) | 0.2 |
Ni (to) | 0.2 |
Other | 0.2 |
P (from) | 0.01 |
P (to) | 0.4 |
Pb (from) | 0.02 |
Pb (to) | 0.02 |
Rest | Cu |
Sn (from) | 7.5 |
Sn (to) | 8.5 |
Zn (from) | 0.2 |
Zn (to) | 0.2 |
suitable according to DIN EN 602 | No |
Material chemically EN 573-3 | Bronze Cu Sn 8 |
Material no | CW453K (2.1030) |
Coefficient of thermal expansion from 20 to 300°C | 18.2 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 400°C | 18.7 K⁻¹10⁻⁶ |
Density | 8.79 g/cm³ |
Modulus of elasticity at 100°C | 106 GPa |
Modulus of elasticity at 20°C | 109 GPa |
Modulus of elasticity at 200°C | 102 GPa |
Modulus of elasticity at 300°C | 98 GPa |
Modulus of elasticity at 400°C | 93 GPa |
Specific electrical conductivity at 20°C | 7.5 m/Ω*mm² |
Specific electrical conductivity at 200°C | 6.5 m/Ω*mm² |
Specific electrical resistance at 20°C | 0.133 Ω*mm²/m |
Specific electrical resistance at 200°C | 6.5 Ω*mm²/m |
Specific heat at 20°C | 0.377 J/(kg·K) |
Thermal conductivity at 20°C | 67 W/m*K |
Thermal conductivity at 200°C | 81 W/m*K |
Brazing | 1 |
Soft soldering | 1 |
Gas | 3 |
MIG | 2 |
Resistance spot welding | 2 |
TIG | 2 |
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified