EN AW-6061
sheet rolled
- Form sheet rolled
- Material Aluminum
- Material EN AW-6061
- Material chemically EN 573-3 Al Mg1 Si Cu
- DIN 3.3211
BIKAR Metals companies
Shipbuilding
Railed vehicles
Boiler and container construction
Aerospace
Military technology
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (from) | 0.04 |
| Cr (to) | 0.35 |
| Cu (from) | 0.15 |
| Cu (to) | 0.4 |
| Fe (to) | 0.7 |
| Mg (from) | 0.8 |
| Mg (to) | 1.2 |
| Mn (to) | 0.15 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.4 |
| Si (to) | 0.8 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 3 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 2 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | water |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 4 |
| Material chemically EN 573-3 | Al Mg1 Si Cu |
| DIN | 3.3211 |
| DIN (old designation) | Al Mg1 Si Cu |
| France AFNOR | A-GSUC |
| Italy UNI | 9006/2 |
| Norway | - |
| Spain | L-3420 |
| Sweden | - |
| United Kingdom BS | H20 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 4 |
| Laminating | 2 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 30 m/Ω*mm² |
| Electrical conductivity min. | 22 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.3 GPa |
| Thermal conductivity max. | 200 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering | 3 |
| Soft soldering with flux | 3 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 1 |
| Plasma | 2 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified