EN AW-2011
hexagon bar drawn
- Form hexagon bar drawn
- Material Aluminum
- Material EN AW-2011
- Material chemically EN 573-3 Al Cu6 Bi Pb
- DIN 3.1655
BIKAR Metals companies
Mechanical Engineering
Automotive
Turned parts
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Bi (from) | 0,2 |
| Bi (to) | 0,6 |
| Co (from) | 0 |
| Co (to) | 0 |
| Cu (from) | 5 |
| Cu (to) | 6 |
| Fe (to) | 0,7 |
| Other | 0,05 |
| Pb (from) | 0,2 |
| Pb (to) | 0,6 |
| Rest | Aluminium |
| Si (to) | 0,4 |
| Total | 0,15 |
| Zn (to) | 0,3 |
0,20 – 0,60 Bi • 0,20 – 0,60 Pb
| Anodising - protective anodising | 4,5 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 3 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 5 |
| Laser cutting | 4,5 |
| Plasma cutting | 4,5 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Extruding | 4 |
| Impact extrusion conditions | O/H111 |
| Upsetting (Conditional) | 3 |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 8 h |
| Heating temperature max. | 185 °C |
| Heating temperature min. | 165 °C |
| Quenching | water to 65°C/h |
| Solution annealing max. | 525 °C |
| Solution annealing min. | 515 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 1 |
| Photo etching | 2 |
| Colorcode | Verkehrsrot (RAL 3020) |
| Material chemically EN 573-3 | Al Cu6 Bi Pb |
| DIN | 3,1655 |
| DIN (old designation) | Al Cu Bi Pb |
| France AFNOR | A-U5PbBi |
| Italy UNI | 9002/5 |
| Norway | 17.107 |
| Spain | L-3192 |
| Sweden | 144.355 |
| United Kingdom BS | FC1 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 3 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 4 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
| Density | 2.82 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 72.5 GPa |
| Shear modulus | 27.3 GPa |
| Specific heat | 864 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 4 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 5 |
| Friction welding | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 5 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Bi (from) | 0,2 |
| Bi (to) | 0,6 |
| Co (from) | 0 |
| Co (to) | 0 |
| Cu (from) | 5 |
| Cu (to) | 6 |
| Fe (to) | 0,7 |
| Other | 0,05 |
| Pb (from) | 0,2 |
| Pb (to) | 0,6 |
| Rest | Aluminium |
| Si (to) | 0,4 |
| Total | 0,15 |
| Zn (to) | 0,3 |
0,20 – 0,60 Bi • 0,20 – 0,60 Pb
| Anodising - protective anodising | 4,5 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 3 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 5 |
| Laser cutting | 4,5 |
| Plasma cutting | 4,5 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Extruding | 4 |
| Impact extrusion conditions | O/H111 |
| Upsetting (Conditional) | 3 |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 8 h |
| Heating temperature max. | 185 °C |
| Heating temperature min. | 165 °C |
| Quenching | water to 65°C/h |
| Solution annealing max. | 525 °C |
| Solution annealing min. | 515 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 1 |
| Photo etching | 2 |
| Colorcode | Verkehrsrot (RAL 3020) |
| Material chemically EN 573-3 | Al Cu6 Bi Pb |
| DIN | 3,1655 |
| DIN (old designation) | Al Cu Bi Pb |
| France AFNOR | A-U5PbBi |
| Italy UNI | 9002/5 |
| Norway | 17.107 |
| Spain | L-3192 |
| Sweden | 144.355 |
| United Kingdom BS | FC1 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 3 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 4 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
| Density | 2.82 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 72.5 GPa |
| Shear modulus | 27.3 GPa |
| Specific heat | 864 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 4 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 5 |
| Friction welding | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 5 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Bi (from) | 0,2 |
| Bi (to) | 0,6 |
| Co (from) | 0 |
| Co (to) | 0 |
| Cu (from) | 5 |
| Cu (to) | 6 |
| Fe (to) | 0,7 |
| Other | 0,05 |
| Pb (from) | 0,2 |
| Pb (to) | 0,6 |
| Rest | Aluminium |
| Si (to) | 0,4 |
| Total | 0,15 |
| Zn (to) | 0,3 |
0,20 – 0,60 Bi • 0,20 – 0,60 Pb
| Anodising - protective anodising | 4,5 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 3 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 5 |
| Laser cutting | 4,5 |
| Plasma cutting | 4,5 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Extruding | 4 |
| Impact extrusion conditions | O/H111 |
| Upsetting (Conditional) | 3 |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 8 h |
| Heating temperature max. | 185 °C |
| Heating temperature min. | 165 °C |
| Quenching | water to 65°C/h |
| Solution annealing max. | 525 °C |
| Solution annealing min. | 515 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 1 |
| Photo etching | 2 |
| Colorcode | Verkehrsrot (RAL 3020) |
| Material chemically EN 573-3 | Al Cu6 Bi Pb |
| DIN | 3,1655 |
| DIN (old designation) | Al Cu Bi Pb |
| France AFNOR | A-U5PbBi |
| Italy UNI | 9002/5 |
| Norway | 17.107 |
| Spain | L-3192 |
| Sweden | 144.355 |
| United Kingdom BS | FC1 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 3 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 4 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
| Density | 2.82 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 72.5 GPa |
| Shear modulus | 27.3 GPa |
| Specific heat | 864 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 4 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 5 |
| Friction welding | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 5 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Bi (from) | 0,2 |
| Bi (to) | 0,6 |
| Co (from) | 0 |
| Co (to) | 0 |
| Cu (from) | 5 |
| Cu (to) | 6 |
| Fe (to) | 0,7 |
| Other | 0,05 |
| Pb (from) | 0,2 |
| Pb (to) | 0,6 |
| Rest | Aluminium |
| Si (to) | 0,4 |
| Total | 0,15 |
| Zn (to) | 0,3 |
0,20 – 0,60 Bi • 0,20 – 0,60 Pb
| Anodising - protective anodising | 4,5 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 3 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 5 |
| Laser cutting | 4,5 |
| Plasma cutting | 4,5 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Extruding | 4 |
| Impact extrusion conditions | O/H111 |
| Upsetting (Conditional) | 3 |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 8 h |
| Heating temperature max. | 185 °C |
| Heating temperature min. | 165 °C |
| Quenching | water to 65°C/h |
| Solution annealing max. | 525 °C |
| Solution annealing min. | 515 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 1 |
| Photo etching | 2 |
| Colorcode | Verkehrsrot (RAL 3020) |
| Material chemically EN 573-3 | Al Cu6 Bi Pb |
| DIN | 3,1655 |
| DIN (old designation) | Al Cu Bi Pb |
| France AFNOR | A-U5PbBi |
| Italy UNI | 9002/5 |
| Norway | 17.107 |
| Spain | L-3192 |
| Sweden | 144.355 |
| United Kingdom BS | FC1 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 3 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 4 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
| Density | 2.82 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 72.5 GPa |
| Shear modulus | 27.3 GPa |
| Specific heat | 864 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 4 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 5 |
| Friction welding | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 5 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Bi (from) | 0,2 |
| Bi (to) | 0,6 |
| Co (from) | 0 |
| Co (to) | 0 |
| Cu (from) | 5 |
| Cu (to) | 6 |
| Fe (to) | 0,7 |
| Other | 0,05 |
| Pb (from) | 0,2 |
| Pb (to) | 0,6 |
| Rest | Aluminium |
| Si (to) | 0,4 |
| Total | 0,15 |
| Zn (to) | 0,3 |
0,20 – 0,60 Bi • 0,20 – 0,60 Pb
| Anodising - protective anodising | 4,5 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 3 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 5 |
| Laser cutting | 4,5 |
| Plasma cutting | 4,5 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Extruding | 4 |
| Impact extrusion conditions | O/H111 |
| Upsetting (Conditional) | 3 |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 8 h |
| Heating temperature max. | 185 °C |
| Heating temperature min. | 165 °C |
| Quenching | water to 65°C/h |
| Solution annealing max. | 525 °C |
| Solution annealing min. | 515 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 1 |
| Photo etching | 2 |
| Colorcode | Verkehrsrot (RAL 3020) |
| Material chemically EN 573-3 | Al Cu6 Bi Pb |
| DIN | 3,1655 |
| DIN (old designation) | Al Cu Bi Pb |
| France AFNOR | A-U5PbBi |
| Italy UNI | 9002/5 |
| Norway | 17.107 |
| Spain | L-3192 |
| Sweden | 144.355 |
| United Kingdom BS | FC1 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 3 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 4 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
| Density | 2.82 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 72.5 GPa |
| Shear modulus | 27.3 GPa |
| Specific heat | 864 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 4 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 5 |
| Friction welding | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 5 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Bi (from) | 0,2 |
| Bi (to) | 0,6 |
| Co (from) | 0 |
| Co (to) | 0 |
| Cu (from) | 5 |
| Cu (to) | 6 |
| Fe (to) | 0,7 |
| Other | 0,05 |
| Pb (from) | 0,2 |
| Pb (to) | 0,6 |
| Rest | Aluminium |
| Si (to) | 0,4 |
| Total | 0,15 |
| Zn (to) | 0,3 |
0,20 – 0,60 Bi • 0,20 – 0,60 Pb
| Anodising - protective anodising | 4,5 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 3 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 5 |
| Laser cutting | 4,5 |
| Plasma cutting | 4,5 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Extruding | 4 |
| Impact extrusion conditions | O/H111 |
| Upsetting (Conditional) | 3 |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 8 h |
| Heating temperature max. | 185 °C |
| Heating temperature min. | 165 °C |
| Quenching | water to 65°C/h |
| Solution annealing max. | 525 °C |
| Solution annealing min. | 515 °C |
| Eroding | 1 |
| Etching | 2 |
| hardened | 1 |
| Photo etching | 2 |
| Colorcode | Verkehrsrot (RAL 3020) |
| Material chemically EN 573-3 | Al Cu6 Bi Pb |
| DIN | 3,1655 |
| DIN (old designation) | Al Cu Bi Pb |
| France AFNOR | A-U5PbBi |
| Italy UNI | 9002/5 |
| Norway | 17.107 |
| Spain | L-3192 |
| Sweden | 144.355 |
| United Kingdom BS | FC1 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 3 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 4 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
| Density | 2.82 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 72.5 GPa |
| Shear modulus | 27.3 GPa |
| Specific heat | 864 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 4 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 5 |
| Friction welding | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 5 |
| TIG | 5 |
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified