EN AW-2011

flat bar

A technical illustration of the product with dimensions of the material EN AW-2011 from the material Aluminum in the shape flat bar
  • Form flat bar
  • Material Aluminum
  • Material EN AW-2011
  • Material chemically EN 573-3 Al Cu6 Bi Pb
  • DIN 3.1655

No product available for your selection.

You can find an overview of all standard dimensions here in our stock list.
Request drawing part
An image of the material EN AW-2011 from the material Aluminum in the shape flat bar
A technical illustration of the product of the material EN AW-2011 from the material Aluminum in the shape flat bar

Areas of application

Mechanical Engineering

Aerospace

Defense Technology

Features of this material

  • Good machinability
  • High strength
  • High fatigue strength

Features of this material

  • Hardenable

Information about the material

  • Aviation
    Aviation No
  • Chemical specifications
    Be (from) 0
    Be (to) 0
    Bi (from) 0.2
    Bi (to) 0.6
    Co (from) 0
    Co (to) 0
    Cu (from) 5
    Cu (to) 6
    Fe (to) 0.7
    Other 0,05
    Pb (from) 0.2
    Pb (to) 0.6
    Rest Aluminium
    Si (to) 0.4
    Total 0,15
    Zn (to) 0.3

    0,20 – 0,60 Bi • 0,20 – 0,60 Pb

  • Chemical surface treatment
    Anodising - protective anodising 4.5
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 5
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 1
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Extruding 4
    Impact extrusion conditions O/H111
    Upsetting (Conditional) 3
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 8 h
    Heating temperature max. 185 °C
    Heating temperature min. 165 °C
    Quenching water to 65°C/h
    Solution annealing max. 525 °C
    Solution annealing min. 515 °C
  • Machining / Machinability
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
  • Material
    Colorcode Verkehrsrot (RAL 3020)
    Material chemically EN 573-3 Al Cu6 Bi Pb
    DIN 3.1655
    DIN (old designation) Al Cu Bi Pb
    France AFNOR A-U5PbBi
    Italy UNI 9002/5
    Norway 17,107
    Spain L-3192
    Sweden 144,355
    United Kingdom BS FC1
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 3
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 4
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 24 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 25 K⁻¹10⁻⁶
    Coefficient of thermal expansion from -50 to 20°C 21.4 K⁻¹10⁻⁶
    Density 2.82 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.3 GPa
    Specific heat 864 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 4
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 5
    Friction welding 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 5
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Be (from) 0
    Be (to) 0
    Bi (from) 0.2
    Bi (to) 0.6
    Co (from) 0
    Co (to) 0
    Cu (from) 5
    Cu (to) 6
    Fe (to) 0.7
    Other 0,05
    Pb (from) 0.2
    Pb (to) 0.6
    Rest Aluminium
    Si (to) 0.4
    Total 0,15
    Zn (to) 0.3

    0,20 – 0,60 Bi • 0,20 – 0,60 Pb

  • Chemical surface treatment
    Anodising - protective anodising 4.5
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 5
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 1
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Extruding 4
    Impact extrusion conditions O/H111
    Upsetting (Conditional) 3
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 8 h
    Heating temperature max. 185 °C
    Heating temperature min. 165 °C
    Quenching water to 65°C/h
    Solution annealing max. 525 °C
    Solution annealing min. 515 °C
  • Machining / Machinability
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
  • Material
    Colorcode Verkehrsrot (RAL 3020)
    Material chemically EN 573-3 Al Cu6 Bi Pb
    DIN 3.1655
    DIN (old designation) Al Cu Bi Pb
    France AFNOR A-U5PbBi
    Italy UNI 9002/5
    Norway 17,107
    Spain L-3192
    Sweden 144,355
    United Kingdom BS FC1
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 3
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 4
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 24 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 25 K⁻¹10⁻⁶
    Coefficient of thermal expansion from -50 to 20°C 21.4 K⁻¹10⁻⁶
    Density 2.82 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.3 GPa
    Specific heat 864 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 4
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 5
    Friction welding 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 5
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Be (from) 0
    Be (to) 0
    Bi (from) 0.2
    Bi (to) 0.6
    Co (from) 0
    Co (to) 0
    Cu (from) 5
    Cu (to) 6
    Fe (to) 0.7
    Other 0,05
    Pb (from) 0.2
    Pb (to) 0.6
    Rest Aluminium
    Si (to) 0.4
    Total 0,15
    Zn (to) 0.3

    0,20 – 0,60 Bi • 0,20 – 0,60 Pb

  • Chemical surface treatment
    Anodising - protective anodising 4.5
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 5
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 1
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Extruding 4
    Impact extrusion conditions O/H111
    Upsetting (Conditional) 3
  • Heat treatment - Softannealing
    Heating time max. 2 h
    Heating time min. 1 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Heat ageing max. 16 h
    Heat ageing min. 8 h
    Heating temperature max. 185 °C
    Heating temperature min. 165 °C
    Quenching water to 65°C/h
    Solution annealing max. 525 °C
    Solution annealing min. 515 °C
  • Machining / Machinability
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
  • Material
    Colorcode Verkehrsrot (RAL 3020)
    Material chemically EN 573-3 Al Cu6 Bi Pb
    DIN 3.1655
    DIN (old designation) Al Cu Bi Pb
    France AFNOR A-U5PbBi
    Italy UNI 9002/5
    Norway 17,107
    Spain L-3192
    Sweden 144,355
    United Kingdom BS FC1
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 3
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 4
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.4 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 24 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 25 K⁻¹10⁻⁶
    Coefficient of thermal expansion from -50 to 20°C 21.4 K⁻¹10⁻⁶
    Density 2.82 g/cm³
    Electrical conductivity max. 32 m/Ω*mm²
    Electrical conductivity min. 24 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.3 GPa
    Specific heat 864 J/(kg·K)
    Thermal conductivity max. 220 W/m*K
    Thermal conductivity min. 170 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 4
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 5
    Friction welding 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 5
    TIG 5

1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified

More questions about BIKAR?

Information about BIKAR, our product range and our service can be found here:

ABOUT OUR COMPANY