EN AW-6060

Doppel-T-Profil

Form Doppel-T-Profil
Material Aluminum
Material EN AW-6060
Material chemically EN 573-3 Al Mg Si
DIN 3.3206

An image of the material EN AW-6060 from the material Aluminum in the shape Doppel-T-Profil

Areas of application

Architecture

Profiles of any kind

Air conditioning

Areas of application

Exhibition stand construction

Truck superstructures

Piping

Areas of application

Printing and paper industry

Features of this material

Good weldability
Good corrosion resistance to sea water and normal atmosphere

Information about the material

Aviation

Chemical specifications

Be (from)	0
Be (to)	0
Co (from)	0
Co (to)	0
Cr (to)	0.05
Cu (to)	0.1
Fe (from)	0.1
Fe (to)	0.3
Mg (from)	0.35
Mg (to)	0.6
Mn (to)	0.1
Other	0,05
Rest	Aluminium
Si (from)	0.3
Si (to)	0.6
Ti (to)	0.1
Total	0,15
Zn (to)	0.15

(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.

Chemical surface treatment

Anodise - decorative	1.5
Anodising - protective anodising	1
Chromating	2
Cleaning / degreasing	2
Hard anodising	2
Phosphating	2
Pickling	2
Shining	3
special anodising quality EQ	1

Corrosion resistance

Normal atmosphere	1
Seawater atmosphere	2

Cutting

Laser cutting	3
Plasma cutting	2
Sawing	2
Shear cutting	2
Waterjet cutting	1

Food industry

suitable according to DIN EN 602

Yes

Forming

Bending	3
Bending delivery conditions	T3 · T4
Drop forging	1
Extruding	1
Impact extrusion	2
Impact extrusion conditions	O
Upsetting (Conditional)	2
Upsetting conditions	O

Heat treatment - Softannealing

Heating time max.	2 h
Heating time min.	1 h
Annealing temperature max.	400 °C
Annealing temperature min.	360 °C
Cooling conditions	Cooling conditions 30°C/h to 250°C, below 250°C in air

Heat treatment - Solution annealing

Cold ageing condition	danach
Cold ageing max.	8 d
Cold ageing min.	5 d
Heat ageing max.	16 h
Heat ageing min.	4 h
Heating temperature max.	190 °C
Heating temperature min.	155 °C
Quenching	water ∙ air
Solution annealing max.	540 °C
Solution annealing min.	525 °C

Machining / Machinability

Eroding	1
Etching	2
hardened	2
Photo etching	2
soft annealed	3.5

Material

Colorcode	neutral
Material chemically EN 573-3	Al Mg Si
DIN	3.3206
DIN (old designation)	Al Mg Si0,5
France AFNOR	A-GS
Italy UNI	9006/1
Norway	17,310
Spain	L-3442
Sweden	144,103

Mechanical surface treatment

Blasting	1
Brushing	3
Dessinating	1
Grinding	3
Polishing	1

Metallic coating

Galvanising	2
Nickel coating	2
Thermal spraying	4

Organic coating

Enamelling	4
Laminating	2
Painting / Coating	1

physical properties

Coefficient of thermal expansion from 20 to 100°C	23.4 K⁻¹10⁻⁶
Coefficient of thermal expansion from 20 to 200°C	24.5 K⁻¹10⁻⁶
Coefficient of thermal expansion from 20 to 300°C	25.6 K⁻¹10⁻⁶
Coefficient of thermal expansion from -50 to 20°C	21.8 K⁻¹10⁻⁶
Density	2.7 g/cm³
Electrical conductivity max.	38 m/Ω*mm²
Electrical conductivity min.	34 m/Ω*mm²
Modulus of elasticity	69.5 GPa
Shear modulus	26.1 GPa
Specific heat	898 J/(kg·K)
Thermal conductivity max.	220 W/m*K
Thermal conductivity min.	200 W/m*K