EN AW-7020
plate rolled
- Form plate rolled
- Material Aluminum
- Material EN AW-7020
- Material chemically EN 573-3 Al Zn4,5 Mg1
- DIN 3.4335
BIKAR Metals companies
Railed vehicles
Military technology
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |
DIN | 3.4335 |
DIN (old designation) | Al Zn4,5 Mg1 |
France AFNOR | A-Z5G |
Italy UNI | 9007/1 |
Norway | 17,410 |
Spain | L-3741 |
Sweden | 144,425 |
United Kingdom BS | H17 |
Blasting | 1 |
Brushing | 2 |
Dessinating | 1 |
Grinding | 2 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 2 |
Coefficient of thermal expansion from 20 to 100°C | 23.1 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 200°C | 24 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from 20 to 300°C | 25 K⁻¹10⁻⁶ |
Coefficient of thermal expansion from -50 to 20°C | 21.4 K⁻¹10⁻⁶ |
Density | 2.77 g/cm³ |
Electrical conductivity max. | 23 m/Ω*mm² |
Electrical conductivity min. | 19 m/Ω*mm² |
Modulus of elasticity | 70 GPa |
Shear modulus | 26.4 GPa |
Specific heat | 875 J/(kg·K) |
Thermal conductivity max. | 160 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 3 |
Laser | 2 |
MIG | 1 |
Resistance spot welding | 5 |
TIG | 2 |
welding additives |
|
Aviation | No |
Cr (from) | 0.1 |
Cr (to) | 0.35 |
Cu (to) | 0.2 |
Fe (to) | 0.4 |
Mg (from) | 1 |
Mg (to) | 1.4 |
Mn (from) | 0.05 |
Mn (to) | 0.5 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0 |
Si (to) | 0.35 |
Ti footnote reference | a) |
Total | 0,15 |
Zn (from) | 4 |
Zn (to) | 5 |
Zr footnote reference | a) |
0,08 – 0,25 Zr + Ti
Anodise - decorative | 3 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 2 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 3 |
Seawater atmosphere | 4 |
Laser cutting | 3 |
Plasma cutting | 3 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 2 |
Deep drawing conditions | O |
Drop forging | 2 |
Extruding | 2 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 2 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 2 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 400 °C |
Cooling conditions |
≤ 30°C/h to 250°C + 3 – 5 hours hold time, below 250°C in air |
Quenching | air |
Solution annealing max. | 485 °C |
Solution annealing min. | 460 °C |
Eroding | 1 |
Etching | 2 |
hardened | 2 |
Photo etching | 2 |
soft annealed | 3 |
Colorcode | Hellrosa (RAL 3015) |
Material chemically EN 573-3 | Al Zn4,5 Mg1 |