EN AW-7022
circular blank
- Form circular blank
- Material Aluminum
- Material EN AW-7022
- Material chemically EN 573-3 Al Zn5 Mg3 Cu
- DIN 3.4345
BIKAR Metals companies
Tool making, mould making and model making
Military technology
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Cr (from) | 0,1 |
| Cr (to) | 0,3 |
| Cu (from) | 0,5 |
| Cu (to) | 1 |
| Fe (to) | 0,5 |
| Mg (from) | 2,6 |
| Mg (to) | 3,7 |
| Mn (from) | 0,1 |
| Mn (to) | 0,4 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0,5 |
| Ti footnote reference | c) |
| Total | max. 0,15 a) b) c) |
| Zn (from) | 4,3 |
| Zn (to) | 5,2 |
| Zr footnote reference | c) |
a) Includes all listed elements for which no limits are specified. b) The sum of these "other impurities" whose mass fraction is individually 0.010% or more is expressed with two decimal places before the sum. c) Zr + Ti max. 0.20
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 4 |
| Laser cutting | 4 |
| Plasma cutting | 3 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Bending | 4,5 |
| Deep drawing (conditional) | 5 |
| Drop forging | 4 |
| Extruding | 4 |
| Impact extrusion | 5 |
| Open die forging | 4 |
| Press | 5 |
| Upsetting (Conditional) | 5 |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cold ageing condition | üblich ist das Warmauslagern |
| Heat ageing max. | 24 h |
| Heat ageing min. | 12 h |
| Heating temperature max. | 125 °C |
| Heating temperature min. | 110 °C |
| Solution annealing max. | 480 °C |
| Solution annealing min. | 470 °C |
| dimensional stability | 1 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| Colorcode | Lichtgrau (RAL 7035) |
| Material chemically EN 573-3 | Al Zn5 Mg3 Cu |
| DIN | 3,4345 |
| DIN (old designation) | Al Zn Mg Cu0,5 |
| France AFNOR | A-Z5GU0,6 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 3 |
| Coefficient of thermal expansion from 20 to 100°C | 23.6 K⁻¹10⁻⁶ |
| Density | 2.78 g/cm³ |
| Electrical conductivity max. | 22 m/Ω*mm² |
| Electrical conductivity min. | 18 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Thermal conductivity max. | 160 W/m*K |
| Thermal conductivity min. | 130 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 5 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 2 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Cr (from) | 0,1 |
| Cr (to) | 0,3 |
| Cu (from) | 0,5 |
| Cu (to) | 1 |
| Fe (to) | 0,5 |
| Mg (from) | 2,6 |
| Mg (to) | 3,7 |
| Mn (from) | 0,1 |
| Mn (to) | 0,4 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0,5 |
| Ti footnote reference | c) |
| Total | max. 0,15 a) b) c) |
| Zn (from) | 4,3 |
| Zn (to) | 5,2 |
| Zr footnote reference | c) |
a) Includes all listed elements for which no limits are specified. b) The sum of these "other impurities" whose mass fraction is individually 0.010% or more is expressed with two decimal places before the sum. c) Zr + Ti max. 0.20
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 4 |
| Laser cutting | 4 |
| Plasma cutting | 3 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Bending | 4,5 |
| Deep drawing (conditional) | 5 |
| Drop forging | 4 |
| Extruding | 4 |
| Impact extrusion | 5 |
| Open die forging | 4 |
| Press | 5 |
| Upsetting (Conditional) | 5 |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cold ageing condition | üblich ist das Warmauslagern |
| Heat ageing max. | 24 h |
| Heat ageing min. | 12 h |
| Heating temperature max. | 125 °C |
| Heating temperature min. | 110 °C |
| Solution annealing max. | 480 °C |
| Solution annealing min. | 470 °C |
| dimensional stability | 1 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| Colorcode | Lichtgrau (RAL 7035) |
| Material chemically EN 573-3 | Al Zn5 Mg3 Cu |
| DIN | 3,4345 |
| DIN (old designation) | Al Zn Mg Cu0,5 |
| France AFNOR | A-Z5GU0,6 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 3 |
| Coefficient of thermal expansion from 20 to 100°C | 23.6 K⁻¹10⁻⁶ |
| Density | 2.78 g/cm³ |
| Electrical conductivity max. | 22 m/Ω*mm² |
| Electrical conductivity min. | 18 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Thermal conductivity max. | 160 W/m*K |
| Thermal conductivity min. | 130 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 5 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 2 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Cr (from) | 0,1 |
| Cr (to) | 0,3 |
| Cu (from) | 0,5 |
| Cu (to) | 1 |
| Fe (to) | 0,5 |
| Mg (from) | 2,6 |
| Mg (to) | 3,7 |
| Mn (from) | 0,1 |
| Mn (to) | 0,4 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0,5 |
| Ti footnote reference | c) |
| Total | max. 0,15 a) b) c) |
| Zn (from) | 4,3 |
| Zn (to) | 5,2 |
| Zr footnote reference | c) |
a) Includes all listed elements for which no limits are specified. b) The sum of these "other impurities" whose mass fraction is individually 0.010% or more is expressed with two decimal places before the sum. c) Zr + Ti max. 0.20
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 4 |
| Laser cutting | 4 |
| Plasma cutting | 3 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Bending | 4,5 |
| Deep drawing (conditional) | 5 |
| Drop forging | 4 |
| Extruding | 4 |
| Impact extrusion | 5 |
| Open die forging | 4 |
| Press | 5 |
| Upsetting (Conditional) | 5 |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cold ageing condition | üblich ist das Warmauslagern |
| Heat ageing max. | 24 h |
| Heat ageing min. | 12 h |
| Heating temperature max. | 125 °C |
| Heating temperature min. | 110 °C |
| Solution annealing max. | 480 °C |
| Solution annealing min. | 470 °C |
| dimensional stability | 1 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| Colorcode | Lichtgrau (RAL 7035) |
| Material chemically EN 573-3 | Al Zn5 Mg3 Cu |
| DIN | 3,4345 |
| DIN (old designation) | Al Zn Mg Cu0,5 |
| France AFNOR | A-Z5GU0,6 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 3 |
| Coefficient of thermal expansion from 20 to 100°C | 23.6 K⁻¹10⁻⁶ |
| Density | 2.78 g/cm³ |
| Electrical conductivity max. | 22 m/Ω*mm² |
| Electrical conductivity min. | 18 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Thermal conductivity max. | 160 W/m*K |
| Thermal conductivity min. | 130 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 5 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 2 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Cr (from) | 0,1 |
| Cr (to) | 0,3 |
| Cu (from) | 0,5 |
| Cu (to) | 1 |
| Fe (to) | 0,5 |
| Mg (from) | 2,6 |
| Mg (to) | 3,7 |
| Mn (from) | 0,1 |
| Mn (to) | 0,4 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0,5 |
| Ti footnote reference | c) |
| Total | max. 0,15 a) b) c) |
| Zn (from) | 4,3 |
| Zn (to) | 5,2 |
| Zr footnote reference | c) |
a) Includes all listed elements for which no limits are specified. b) The sum of these "other impurities" whose mass fraction is individually 0.010% or more is expressed with two decimal places before the sum. c) Zr + Ti max. 0.20
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 4 |
| Laser cutting | 4 |
| Plasma cutting | 3 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Bending | 4,5 |
| Deep drawing (conditional) | 5 |
| Drop forging | 4 |
| Extruding | 4 |
| Impact extrusion | 5 |
| Open die forging | 4 |
| Press | 5 |
| Upsetting (Conditional) | 5 |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cold ageing condition | üblich ist das Warmauslagern |
| Heat ageing max. | 24 h |
| Heat ageing min. | 12 h |
| Heating temperature max. | 125 °C |
| Heating temperature min. | 110 °C |
| Solution annealing max. | 480 °C |
| Solution annealing min. | 470 °C |
| dimensional stability | 1 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| Colorcode | Lichtgrau (RAL 7035) |
| Material chemically EN 573-3 | Al Zn5 Mg3 Cu |
| DIN | 3,4345 |
| DIN (old designation) | Al Zn Mg Cu0,5 |
| France AFNOR | A-Z5GU0,6 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 3 |
| Coefficient of thermal expansion from 20 to 100°C | 23.6 K⁻¹10⁻⁶ |
| Density | 2.78 g/cm³ |
| Electrical conductivity max. | 22 m/Ω*mm² |
| Electrical conductivity min. | 18 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Thermal conductivity max. | 160 W/m*K |
| Thermal conductivity min. | 130 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 5 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 2 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Cr (from) | 0,1 |
| Cr (to) | 0,3 |
| Cu (from) | 0,5 |
| Cu (to) | 1 |
| Fe (to) | 0,5 |
| Mg (from) | 2,6 |
| Mg (to) | 3,7 |
| Mn (from) | 0,1 |
| Mn (to) | 0,4 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0,5 |
| Ti footnote reference | c) |
| Total | max. 0,15 a) b) c) |
| Zn (from) | 4,3 |
| Zn (to) | 5,2 |
| Zr footnote reference | c) |
a) Includes all listed elements for which no limits are specified. b) The sum of these "other impurities" whose mass fraction is individually 0.010% or more is expressed with two decimal places before the sum. c) Zr + Ti max. 0.20
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 4 |
| Laser cutting | 4 |
| Plasma cutting | 3 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Bending | 4,5 |
| Deep drawing (conditional) | 5 |
| Drop forging | 4 |
| Extruding | 4 |
| Impact extrusion | 5 |
| Open die forging | 4 |
| Press | 5 |
| Upsetting (Conditional) | 5 |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cold ageing condition | üblich ist das Warmauslagern |
| Heat ageing max. | 24 h |
| Heat ageing min. | 12 h |
| Heating temperature max. | 125 °C |
| Heating temperature min. | 110 °C |
| Solution annealing max. | 480 °C |
| Solution annealing min. | 470 °C |
| dimensional stability | 1 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| Colorcode | Lichtgrau (RAL 7035) |
| Material chemically EN 573-3 | Al Zn5 Mg3 Cu |
| DIN | 3,4345 |
| DIN (old designation) | Al Zn Mg Cu0,5 |
| France AFNOR | A-Z5GU0,6 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 3 |
| Coefficient of thermal expansion from 20 to 100°C | 23.6 K⁻¹10⁻⁶ |
| Density | 2.78 g/cm³ |
| Electrical conductivity max. | 22 m/Ω*mm² |
| Electrical conductivity min. | 18 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Thermal conductivity max. | 160 W/m*K |
| Thermal conductivity min. | 130 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 5 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 2 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Cr (from) | 0,1 |
| Cr (to) | 0,3 |
| Cu (from) | 0,5 |
| Cu (to) | 1 |
| Fe (to) | 0,5 |
| Mg (from) | 2,6 |
| Mg (to) | 3,7 |
| Mn (from) | 0,1 |
| Mn (to) | 0,4 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0,5 |
| Ti footnote reference | c) |
| Total | max. 0,15 a) b) c) |
| Zn (from) | 4,3 |
| Zn (to) | 5,2 |
| Zr footnote reference | c) |
a) Includes all listed elements for which no limits are specified. b) The sum of these "other impurities" whose mass fraction is individually 0.010% or more is expressed with two decimal places before the sum. c) Zr + Ti max. 0.20
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 4 |
| Laser cutting | 4 |
| Plasma cutting | 3 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Bending | 4,5 |
| Deep drawing (conditional) | 5 |
| Drop forging | 4 |
| Extruding | 4 |
| Impact extrusion | 5 |
| Open die forging | 4 |
| Press | 5 |
| Upsetting (Conditional) | 5 |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cold ageing condition | üblich ist das Warmauslagern |
| Heat ageing max. | 24 h |
| Heat ageing min. | 12 h |
| Heating temperature max. | 125 °C |
| Heating temperature min. | 110 °C |
| Solution annealing max. | 480 °C |
| Solution annealing min. | 470 °C |
| dimensional stability | 1 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| Colorcode | Lichtgrau (RAL 7035) |
| Material chemically EN 573-3 | Al Zn5 Mg3 Cu |
| DIN | 3,4345 |
| DIN (old designation) | Al Zn Mg Cu0,5 |
| France AFNOR | A-Z5GU0,6 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 3 |
| Coefficient of thermal expansion from 20 to 100°C | 23.6 K⁻¹10⁻⁶ |
| Density | 2.78 g/cm³ |
| Electrical conductivity max. | 22 m/Ω*mm² |
| Electrical conductivity min. | 18 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Thermal conductivity max. | 160 W/m*K |
| Thermal conductivity min. | 130 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 5 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 2 |
| TIG | 5 |
| Aviation | No |
| Be (from) | 0 |
| Be (to) | 0 |
| Cr (from) | 0,1 |
| Cr (to) | 0,3 |
| Cu (from) | 0,5 |
| Cu (to) | 1 |
| Fe (to) | 0,5 |
| Mg (from) | 2,6 |
| Mg (to) | 3,7 |
| Mn (from) | 0,1 |
| Mn (to) | 0,4 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0,5 |
| Ti footnote reference | c) |
| Total | max. 0,15 a) b) c) |
| Zn (from) | 4,3 |
| Zn (to) | 5,2 |
| Zr footnote reference | c) |
a) Includes all listed elements for which no limits are specified. b) The sum of these "other impurities" whose mass fraction is individually 0.010% or more is expressed with two decimal places before the sum. c) Zr + Ti max. 0.20
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 4 |
| Laser cutting | 4 |
| Plasma cutting | 3 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Bending | 4,5 |
| Deep drawing (conditional) | 5 |
| Drop forging | 4 |
| Extruding | 4 |
| Impact extrusion | 5 |
| Open die forging | 4 |
| Press | 5 |
| Upsetting (Conditional) | 5 |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cold ageing condition | üblich ist das Warmauslagern |
| Heat ageing max. | 24 h |
| Heat ageing min. | 12 h |
| Heating temperature max. | 125 °C |
| Heating temperature min. | 110 °C |
| Solution annealing max. | 480 °C |
| Solution annealing min. | 470 °C |
| dimensional stability | 1 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| Colorcode | Lichtgrau (RAL 7035) |
| Material chemically EN 573-3 | Al Zn5 Mg3 Cu |
| DIN | 3,4345 |
| DIN (old designation) | Al Zn Mg Cu0,5 |
| France AFNOR | A-Z5GU0,6 |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 3 |
| Coefficient of thermal expansion from 20 to 100°C | 23.6 K⁻¹10⁻⁶ |
| Density | 2.78 g/cm³ |
| Electrical conductivity max. | 22 m/Ω*mm² |
| Electrical conductivity min. | 18 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Thermal conductivity max. | 160 W/m*K |
| Thermal conductivity min. | 130 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 5 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 2 |
| TIG | 5 |
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified