EN AW-2024
ring
- Form ring
- Material Aluminum
- Material EN AW-2024
- Material chemically EN 573-3 Al Cu4 Mg1
- DIN 3.1355
| Aviation | No |
| Cr (to) | 0,1 |
| Cu (from) | 3,8 |
| Cu (to) | 4,9 |
| Fe (to) | 0,5 |
| Mg (from) | 1,2 |
| Mg (to) | 1,8 |
| Mn (from) | 0,3 |
| Mn (to) | 0,9 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0,5 |
| Ti footnote reference | f) |
| Ti (to) | 0,15 |
| Total | 0,15 a) b) f) |
| Zn (to) | 0,25 |
| Zr footnote reference | f) |
a) Includes all listed elements for which no limits are specified. b) The sum of these "other additions", whose mass fraction is individually 0.010% or more, is expressed with two decimal places before the sum. f) A sum limit for Zr + Ti of 0.25 max. applies to forged or extruded products, if this value has been agreed between supplier and buyer.
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 3 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4,5 |
| Normal atmosphere | 4 |
| Seawater atmosphere | 4 |
| Laser cutting | 4,5 |
| Plasma cutting | 4,5 |
| Sawing | 2 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| Bending | 4 |
| Bending delivery conditions | O |
| Deep drawing (conditional) | 3 |
| Deep drawing conditions | O |
| Drop forging | 4 |
| Extruding | 5 |
| Impact extrusion | 4 |
| Impact extrusion conditions | O |
| Open die forging | 3 |
| Press | 3 |
| Press conditions | O |
| Upsetting (Conditional) | 4 |
| Upsetting conditions | O |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
| Cold ageing condition | Storage at room temperature T3...; T4...., or |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 24 h |
| Heat ageing min. | 16 h |
| Heating temperature max. | 195 °C |
| Heating temperature min. | 180 °C |
| Quenching | water |
| Heating time max. | 3 h |
| Heating time min. | 2 h |
| Solution annealing max. | 505 °C |
| Solution annealing min. | 495 °C |
| dimensional stability | 4 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 2 |
| Photo etching | 2 |
| soft annealed | 3 |
| Colorcode | Reinorange (RAL 2004) |
| Material chemically EN 573-3 | Al Cu4 Mg1 |
| DIN | 3,1355 |
| DIN (old designation) | Al Cu Mg2 |
| France AFNOR | A-U4G1 |
| Italy UNI | 9002/4 |
| Norway | - |
| Spain | L-3140 |
| Sweden | - |
| United Kingdom BS | L97 |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 1 |
| Galvanising | 2 |
| Nickel coating | 1 |
| Thermal spraying | 3 |
| Enamelling | 5 |
| Laminating | 2 |
| Painting / Coating | 3 |
| Coefficient of thermal expansion from 20 to 100°C | 22.9 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C | 23.8 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C | 24.7 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from -50 to 20°C | 21.1 K⁻¹10⁻⁶ |
| Density | 2.77 g/cm³ |
| Electrical conductivity max. | 21 m/Ω*mm² |
| Electrical conductivity min. | 18 m/Ω*mm² |
| Modulus of elasticity | 73 GPa |
| Shear modulus | 27.4 GPa |
| Specific heat | 875 J/(kg·K) |
| Thermal conductivity max. | 150 W/m*K |
| Thermal conductivity min. | 130 W/m*K |
| Brazing | 5 |
| Brazing with flux | 5 |
| Friction soldering | 3 |
| Soft soldering | 5 |
| Soft soldering with flux | 5 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 5 |
| MIG | 5 |
| Plasma | 5 |
| Resistance spot welding | 1 |
| TIG | 5 |
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified