EN AW-2017A

Roundbar (drawn)

A technical illustration of the product with dimensions of the material EN AW-2017A from the material Aluminum in the shape Roundbar (drawn)
  • Form Roundbar (drawn)
  • Material Aluminum
  • Material EN AW-2017A
  • Material chemically EN 573-3 Al Cu4 Mg Si(A)
  • DIN 3.1325

No product available for your selection.

You can find an overview of all standard dimensions here in our stock list.
Request drawing part
An image of the material EN AW-2017A from the material Aluminum in the shape Roundbar (drawn)
A technical illustration of the product of the material EN AW-2017A from the material Aluminum in the shape Roundbar (drawn)

Areas of application

Machine construction

High-strength constructions

Aerospace

Areas of application

Military technology

Features of this material

  • Very good machinability
  • High strength
  • High fatigue strength

Features of this material

  • Curable

Information about the material

  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5

1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified

More questions about BIKAR?

Information about BIKAR, our product range and our service can be found here:

ABOUT OUR COMPANY