EN AW-2017A
circular blank
![A technical illustration of the product with dimensions of the material EN AW-2017A from the material Aluminum in the shape circular blank](https://my.bikar.com/media/cache/sylius_shop_product_detail_pictogram_thumbnail/6b/b1/00a1ff6f588d63eea0a03bb32b87.jpg)
- Form circular blank
- Material Aluminum
- Material EN AW-2017A
- Material chemically EN 573-3 Al Cu4 Mg Si(A)
- DIN 3.1325
![An image of the material EN AW-2017A from the material Aluminum in the shape circular blank](https://my.bikar.com/media/cache/sylius_shop_product_detail_mainimage_thumbnail/e9/bf/fdbd612f678c74ee1798d11c3bee.jpg)
![A technical illustration of the product of the material EN AW-2017A from the material Aluminum in the shape circular blank](https://my.bikar.com/media/cache/sylius_shop_product_detail_media_medium_thumbnail/83/0b/f226c09a4ab901e7168707cce79d.jpg)
BIKAR Metals companies
Machine construction
High-strength constructions
Aerospace
Military technology
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
Aviation | No |
Cr (to) | 0.1 |
Cu (from) | 3.5 |
Cu (to) | 4.5 |
Fe (to) | 0.7 |
Mg (from) | 0.4 |
Mg (to) | 1 |
Mn (from) | 0.4 |
Mn (to) | 1 |
Other | 0,05 |
Rest | Aluminium |
Si (from) | 0.2 |
Si (to) | 0.8 |
Total | 0,15 |
Zn (to) | 0.25 |
0,25 Zr+Ti
Anodise - decorative | 5 |
Anodising - protective anodising | 2 |
Chromating | 2 |
Cleaning / degreasing | 2 |
Hard anodising | 3 |
Phosphating | 2 |
Pickling | 2 |
Shining | 4.5 |
Normal atmosphere | 4 |
Seawater atmosphere | 4 |
Laser cutting | 4.5 |
Plasma cutting | 4.5 |
Sawing | 2 |
Shear cutting | 2 |
Waterjet cutting | 1 |
suitable according to DIN EN 602 | No |
Bending | 2 |
Bending delivery conditions | O |
Deep drawing (conditional) | 3 |
Deep drawing conditions | O |
Drop forging | 3 |
Extruding | 4 |
Impact extrusion | 3 |
Impact extrusion conditions | O |
Open die forging | 3 |
Press | 3 |
Press conditions | O |
Upsetting (Conditional) | 3 |
Upsetting conditions | O |
Heating time max. | 3 h |
Heating time min. | 2 h |
Annealing temperature max. | 420 °C |
Annealing temperature min. | 380 °C |
Cooling conditions |
Cooling conditions 30°C/h to 250°C, below 250°C in air |
Cold ageing max. | 8 d |
Cold ageing min. | 5 d |
Quenching | water |
Heating time max. | 3 h |
Heating time min. | 2 h |
Solution annealing max. | 505 °C |
Solution annealing min. | 495 °C |
cold worked | 3 |
dimensional stability | 4 |
Eroding | 1 |
Etching | 2 |
hardened | 1 |
Photo etching | 2 |
soft annealed | 4 |
Colorcode | Laubgrün (RAL 6002) |
Material chemically EN 573-3 | Al Cu4 Mg Si(A) |
DIN | 3.1325 |
DIN (old designation) | Al Cu Mg1 |
France AFNOR | A-U4G |
Italy UNI | 9002/2 |
Norway | - |
Spain | L-3120 |
Sweden | - |
United Kingdom BS | - |
Blasting | 1 |
Brushing | 2 |
Grinding | 2 |
Polishing | 1 |
Galvanising | 2 |
Nickel coating | 2 |
Thermal spraying | 4 |
Enamelling | 5 |
Laminating | 2 |
Painting / Coating | 3 |
Coefficient of thermal expansion from 20 to 100°C | 23 K⁻¹10⁻⁶ |
Density | 2.8 g/cm³ |
Electrical conductivity max. | 28 m/Ω*mm² |
Electrical conductivity min. | 18 m/Ω*mm² |
Modulus of elasticity | 72.5 GPa |
Shear modulus | 27.2 GPa |
Thermal conductivity max. | 200 W/m*K |
Thermal conductivity min. | 130 W/m*K |
Brazing | 5 |
Brazing with flux | 5 |
Friction soldering | 3 |
Soft soldering | 5 |
Soft soldering with flux | 5 |
Friction stir welding | 2 |
Friction welding | 2 |
Gas | 5 |
Laser | 5 |
MIG | 5 |
Plasma | 5 |
Resistance spot welding | 1 |
TIG | 5 |
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified