EN AW-2017A

sheet rolled

A technical illustration of the product with dimensions of the material EN AW-2017A from the material Aluminum in the shape sheet rolled
  • Form sheet rolled
  • Material Aluminum
  • Material EN AW-2017A
  • Material chemically EN 573-3 Al Cu4 Mg Si(A)
  • DIN 3.1325

No product available for your selection.

An image of the material EN AW-2017A from the material Aluminum in the shape sheet rolled
A technical illustration of the product of the material EN AW-2017A from the material Aluminum in the shape sheet rolled

Areas of application

Machine construction

High-strength constructions

Aerospace

Areas of application

Military technology

Features of this material

  • Very good machinability
  • High strength
  • High fatigue strength

Features of this material

  • Curable

Information about the material

  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2
    Thermal spraying 4
  • Organic coating
    Enamelling 5
    Laminating 2
    Painting / Coating 3
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23 K⁻¹10⁻⁶
    Density 2.8 g/cm³
    Electrical conductivity max. 28 m/Ω*mm²
    Electrical conductivity min. 18 m/Ω*mm²
    Modulus of elasticity 72.5 GPa
    Shear modulus 27.2 GPa
    Thermal conductivity max. 200 W/m*K
    Thermal conductivity min. 130 W/m*K
  • Soldering
    Brazing 5
    Brazing with flux 5
    Friction soldering 3
    Soft soldering 5
    Soft soldering with flux 5
  • Welding
    Friction stir welding 2
    Friction welding 2
    Gas 5
    Laser 5
    MIG 5
    Plasma 5
    Resistance spot welding 1
    TIG 5
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.1
    Cu (from) 3.5
    Cu (to) 4.5
    Fe (to) 0.7
    Mg (from) 0.4
    Mg (to) 1
    Mn (from) 0.4
    Mn (to) 1
    Other 0,05
    Rest Aluminium
    Si (from) 0.2
    Si (to) 0.8
    Total 0,15
    Zn (to) 0.25

    0,25 Zr+Ti

  • Chemical surface treatment
    Anodise - decorative 5
    Anodising - protective anodising 2
    Chromating 2
    Cleaning / degreasing 2
    Hard anodising 3
    Phosphating 2
    Pickling 2
    Shining 4.5
  • Corrosion resistance
    Normal atmosphere 4
    Seawater atmosphere 4
  • Cutting
    Laser cutting 4.5
    Plasma cutting 4.5
    Sawing 2
    Shear cutting 2
    Waterjet cutting 1
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 2
    Bending delivery conditions O
    Deep drawing (conditional) 3
    Deep drawing conditions O
    Drop forging 3
    Extruding 4
    Impact extrusion 3
    Impact extrusion conditions O
    Open die forging 3
    Press 3
    Press conditions O
    Upsetting (Conditional) 3
    Upsetting conditions O
  • Heat treatment - Softannealing
    Heating time max. 3 h
    Heating time min. 2 h
    Annealing temperature max. 420 °C
    Annealing temperature min. 380 °C
    Cooling conditions Cooling conditions 30°C/h to
    250°C, below 250°C in air
  • Heat treatment - Solution annealing
    Cold ageing max. 8 d
    Cold ageing min. 5 d
    Quenching water
    Heating time max. 3 h
    Heating time min. 2 h
    Solution annealing max. 505 °C
    Solution annealing min. 495 °C
  • Machining / Machinability
    cold worked 3
    dimensional stability 4
    Eroding 1
    Etching 2
    hardened 1
    Photo etching 2
    soft annealed 4
  • Material
    Colorcode Laubgrün (RAL 6002)
    Material chemically EN 573-3 Al Cu4 Mg Si(A)
    DIN 3.1325
    DIN (old designation) Al Cu Mg1
    France AFNOR A-U4G
    Italy UNI 9002/2
    Norway -
    Spain L-3120
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Blasting 1
    Brushing 2
    Grinding 2
    Polishing 1
  • Metallic coating
    Galvanising 2
    Nickel coating 2