FORMODAL BM-5083 Walzplatte
EN AW-5083
Ring - machined surface
- Form Ring - machined surface
- Material Aluminum
- Material EN AW-5083
- Material chemically EN 573-3 Al Mg4,5 Mn0,7
- DIN 3.3547
EN AW-5083
| Aviation | No |
| Cr (from) | 0.05 |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.4 |
| Mg (from) | 4 |
| Mg (to) | 4.9 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (to) | 0.4 |
| Ti (to) | 0.15 |
| Total | 0,15 |
| Zn (to) | 0.25 |
(a) Includes all listed elements for which no limits are given. (b) The sum of these 'other impurities', the mass fraction of which is individually 0,010 % or more, is expressed with two decimal places before the summation.
| Anodise - decorative | 4 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 1 |
| Laser cutting | 4 |
| Plasma cutting | 2 |
| Sawing | 3 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | Yes |
| Bending | 2 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 4 |
| Extruding | 4 |
| Impact extrusion | 4 |
| Open die forging | 4 |
| Press | 4 |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions | 30°C/h - 50°C/h |
| cold worked | 2 |
| dimensional stability | 2 |
| Eroding | 1 |
| Etching | 2 |
| Photo etching | 2 |
| soft annealed | 3 |
| Colorcode | Signalbraun (RAL 8002) |
| Material chemically EN 573-3 | Al Mg4,5 Mn0,7 |
| DIN | 3.3547 |
| DIN (old designation) | Al Mg4,5 Mn |
| France AFNOR | A-G4,5MC |
| Italy UNI | 9005/5 |
| Norway | 17,215 |
| Spain | L-3321 |
| Sweden | 144,140 |
| United Kingdom BS | N8 |
| Shape specific material | FORMODAL BM-5083 Walzplatte |
| Blasting | 1 |
| Brushing | 2 |
| Dessinating | 1 |
| Grinding | 2 |
| Polishing | 2 |
| Galvanising | 2 |
| Nickel coating | 1 |
| Thermal spraying | 3 |
| Enamelling | 3 |
| Laminating | 2 |
| Painting / Coating | 4 |
| Coefficient of thermal expansion from 20 to 100°C | 24.2 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C | 25 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C | 26 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from -50 to 20°C | 22.3 K⁻¹10⁻⁶ |
| Density | 2.66 g/cm³ |
| Electrical conductivity max. | 19 m/Ω*mm² |
| Electrical conductivity min. | 16 m/Ω*mm² |
| Modulus of elasticity | 71 GPa |
| Shear modulus | 26.8 GPa |
| Specific heat | 900 J/(kg·K) |
| Thermal conductivity max. | 140 W/m*K |
| Thermal conductivity min. | 110 W/m*K |
| Brazing | 4 |
| Brazing with flux | 4 |
| Friction soldering | 3 |
| Soft soldering | 5 |
| Soft soldering with flux | 4 |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 3 |
| Laser | 2 |
| MIG | 2 |
| Plasma | 2 |
| Resistance spot welding | 2 |
| TIG | 2 |
| welding additives |
|
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified