EN AW-6082
plate rolled
- Form plate rolled
- Material Aluminum
- Material EN AW-6082
- Material chemically EN 573-3 Al Si1 Mg Mn
- DIN 3.2315
BIKAR Metals companies
Shipbuilding
Railed vehicles
Boiler and container construction
Aerospace
Military technology
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
| Aviation | No |
| Cr (to) | 0.25 |
| Cu (to) | 0.1 |
| Fe (to) | 0.5 |
| Mg (from) | 0.6 |
| Mg (to) | 1.2 |
| Mn (from) | 0.4 |
| Mn (to) | 1 |
| Other | 0,05 |
| Rest | Aluminium |
| Si (from) | 0.7 |
| Si (to) | 1.3 |
| Ti (to) | 0.1 |
| Total | 0,15 |
| Zn (to) | 0.2 |
(a) Includes all listed elements for which no limits are specified. (b) The sum of these "other impurities" whose mass fraction is individually 0,010 % or more is expressed with two decimal places before the summation.
| Anodise - decorative | 3 |
| Anodising - protective anodising | 1 |
| Normal atmosphere | 1 |
| Seawater atmosphere | 2 |
| suitable according to DIN EN 602 | Yes |
| Bending | 3 |
| Bending delivery conditions | T3 · T4 |
| Deep drawing (conditional) | 2 |
| Deep drawing conditions | O |
| Drop forging | 2 |
| Extruding | 2 |
| Impact extrusion | 2 |
| Impact extrusion conditions | O |
| Open die forging | 2 |
| Press | 2 |
| Press conditions | O |
| Upsetting (Conditional) | 2 |
| Upsetting conditions | O |
| Heating time max. | 2 h |
| Heating time min. | 1 h |
| Annealing temperature max. | 420 °C |
| Annealing temperature min. | 380 °C |
| Cooling conditions |
≤ 30°C/h up to 250°C, below 250°C in the air |
| Cold ageing max. | 8 d |
| Cold ageing min. | 5 d |
| Heat ageing max. | 16 h |
| Heat ageing min. | 4 h |
| Heating temperature max. | 190 °C |
| Heating temperature min. | 155 °C |
| Quenching | Water, Air |
| Solution annealing max. | 540 °C |
| Solution annealing min. | 525 °C |
| dimensional stability | 3 |
| Eroding | 1 |
| hardened | 2 |
| soft annealed | 4 |
| Colorcode | Enzianblau (RAL 5010) |
| Material chemically EN 573-3 | Al Si1 Mg Mn |
| DIN | 3.2315 |
| DIN (old designation) | Al Mg Si1 |
| France AFNOR | A-SGM0,7 |
| Italy UNI | 9006/4 |
| Norway | - |
| Spain | L-3453 |
| Sweden | 144,212 |
| United Kingdom BS | H30 |
| Polishing | 1 |
| Painting / Coating | 2 |
| Coefficient of thermal expansion from 20 to 100°C | 23.4 K⁻¹10⁻⁶ |
| Density | 2.7 g/cm³ |
| Electrical conductivity max. | 32 m/Ω*mm² |
| Electrical conductivity min. | 24 m/Ω*mm² |
| Modulus of elasticity | 70 GPa |
| Shear modulus | 26.4 GPa |
| Specific heat | 896 J/(kg·K) |
| Thermal conductivity max. | 220 W/m*K |
| Thermal conductivity min. | 170 W/m*K |
| Brazing | 4 |
| Brazing with flux | 3 |
| Friction soldering | 2 |
| Soft soldering with flux | 3 |
| Gas | 3 |
| MIG | 1 |
| Resistance spot welding | 3 |
| TIG | 2 |
| welding additives |
|
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified