CW508L

flat bar drawn

[208_305]
  • Form flat bar drawn
  • Material Brass
  • Material CW508L
  • Material chemically EN 573-3 Brass Ms 63/Cu Zn 37

No product available for your selection.

[208_305]
[208_305]

Areas of application

Sanitary fittings, bathroom equipment

Water boxes for car radiators

Contact parts

Areas of application

Pneumatic cylinders

Parts for brass instruments, organ components

Features of this material

  • good resistance to water, water vapour, various salt solutions, many organic liquids

Information about the material

  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Brass Ms 63/Cu Zn 37
    Material no CW508L (former.: 2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3
  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Brass Ms 63/Cu Zn 37
    Material no CW508L (former.: 2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3
  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Brass Ms 63/Cu Zn 37
    Material no CW508L (former.: 2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3
  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Brass Ms 63/Cu Zn 37
    Material no CW508L (former.: 2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3
  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Brass Ms 63/Cu Zn 37
    Material no CW508L (former.: 2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3
  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Brass Ms 63/Cu Zn 37
    Material no CW508L (former.: 2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3
  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Brass Ms 63/Cu Zn 37
    Material no CW508L (former.: 2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3
  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Brass Ms 63/Cu Zn 37
    Material no CW508L (former.: 2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3

1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified