brass CW508L

sheet rolled

A technical illustration of the product with dimensions of the material brass CW508L from the material Brass in the shape sheet rolled
  • Form sheet rolled
  • Material Brass
  • Material brass CW508L
  • Material chemically EN 573-3 Ms 63 / CuZn37
An image of the material brass CW508L from the material Brass in the shape sheet rolled
A technical illustration of the product of the material brass CW508L from the material Brass in the shape sheet rolled

Areas of application

Sanitary fittings, bathroom equipment

Water boxes for car radiators

Contact parts

Areas of application

Pneumatic cylinders

Parts for brass instruments, organ components

Features of this material

  • good resistance to water, water vapour, various salt solutions, many organic liquids

Information about the material

  • Aviation
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (to) 64
    Fe (from) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (to) 0.3
    Other 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Rest Zn
    Sn (from) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 2
    MIG 3
    Resistance spot welding 2
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3
  • Aviation
    Aviation No
    Aviation No
  • Chemical specifications
    Al (from) 0.05
    Al (from) 0.05
    Al (to) 0.05
    Al (to) 0.05
    Cu (from) 62
    Cu (from) 62
    Cu (to) 64
    Cu (to) 64
    Fe (from) 0.1
    Fe (from) 0.1
    Fe (to) 0.1
    Fe (to) 0.1
    Ni (from) 0.3
    Ni (from) 0.3
    Ni (to) 0.3
    Ni (to) 0.3
    Other 0.1
    Other 0.1
    Pb (from) 0.1
    Pb (from) 0.1
    Pb (to) 0.1
    Pb (to) 0.1
    Rest Zn
    Rest Zn
    Sn (from) 0.1
    Sn (from) 0.1
    Sn (to) 0.1
    Sn (to) 0.1
  • Food industry
    suitable according to DIN EN 602 No
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material chemically EN 573-3 Ms 63 / CuZn37
    Material no CW508L (2.0321)
    Material no CW508L (2.0321)
  • physical properties
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 21 K⁻¹10⁻⁶
    Density 8.44 g/cm³
    Density 8.44 g/cm³
    Modulus of elasticity at 20°C 110 GPa
    Modulus of elasticity at 20°C 110 GPa
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 20°C 15 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical conductivity at 200°C 12 m/Ω*mm²
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 20°C 0.066 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific electrical resistance at 200°C 0.083 Ω*mm²/m
    Specific heat at 20°C 0.377 J/(kg·K)
    Specific heat at 20°C 0.377 J/(kg·K)
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 20°C 120 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at 200°C 142 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
    Thermal conductivity at -200°C 50 W/m*K
  • Soldering
    Brazing 1
    Brazing 1
    Soft soldering 1
    Soft soldering 1
  • Welding
    Gas 2
    Gas 2
    MIG 3
    MIG 3
    Resistance spot welding 2
    Resistance spot welding 2
    TIG 3
    TIG 3

1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified

More questions about BIKAR?

Information about BIKAR, our product range and our service can be found here:

ABOUT OUR COMPANY