CW009A

Round bar

[109_003]
  • Form Round bar
  • Material Copper
  • Material CW009A
  • Material chemically EN 573-3 OFE-Cu/Oxygen-free

No product available for your selection.

[109_003]
[109_003]

Information about the material

  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2
  • Aviation
    Aviation No
  • Chemical specifications
    Ag (from) 0.0025
    Ag (to) 0.0025
    Cu footnote reference Diese Kupfersorte wird aus Cu-CATH-1 (CR001A) nach DIN EN 1978 hergestellt.
    Fe (from) 0.001
    Fe (to) 0.001
    Ni (from) 0.001
    Ni (to) 0.001
    P (from) 0.0003
    P (to) 0.0003
    Rest Cu
    S (from) 0.0015
    S (to) 0.0015
  • Food industry
    suitable according to DIN EN 602 No
  • Material
    Material chemically EN 573-3 OFE-Cu/Oxygen-free
    Material no CW009A
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 17 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 200°C 17.3 K⁻¹10⁻⁶
    Coefficient of thermal expansion from 20 to 300°C 17.7 K⁻¹10⁻⁶
    Density 8.94 g/cm³
    Modulus of elasticity at 100°C 124 GPa
    Modulus of elasticity at 20°C 118 GPa
    Modulus of elasticity at 200°C 122 GPa
    Specific electrical conductivity at 100°C 44 m/Ω*mm²
    Specific electrical conductivity at 20°C 58 m/Ω*mm²
    Specific electrical conductivity at 200°C 34 m/Ω*mm²
    Specific electrical conductivity at -100°C 110 m/Ω*mm²
    Specific electrical conductivity at -200°C 460 m/Ω*mm²
    Specific electrical resistance at 100°C 0.023 Ω*mm²/m
    Specific electrical resistance at 20°C 0.017 Ω*mm²/m
    Specific electrical resistance at 200°C 0.029 Ω*mm²/m
    Specific electrical resistance at -100°C 0.009 Ω*mm²/m
    Specific electrical resistance at -200°C 0.002 Ω*mm²/m
    Specific heat at 100°C 0.39 J/(kg·K)
    Specific heat at 20°C 0.39 J/(kg·K)
    Specific heat at 200°C 0.4 J/(kg·K)
    Thermal conductivity at 100°C 386 W/m*K
    Thermal conductivity at 20°C 393 W/m*K
    Thermal conductivity at 200°C 381 W/m*K
    Thermal conductivity at -100°C 436 W/m*K
    Thermal conductivity at -200°C 519 W/m*K
  • Soldering
    Brazing 1
    Soft soldering 1
  • Welding
    Gas 4
    Laser 2
    MIG 2
    Resistance spot welding 5
    TIG 2

1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified