FORMODAL®060

circular blank

A technical illustration of the product with dimensions of the material FORMODAL®060 from the material Aluminum in the shape circular blank
  • Form circular blank
  • Material Aluminum
  • Material FORMODAL®060
  • Material chemically EN 573-3 7050
  • DIN -

No product available for your selection.

An image of the material FORMODAL®060 from the material Aluminum in the shape circular blank
A technical illustration of the product of the material FORMODAL®060 from the material Aluminum in the shape circular blank

Areas of application

Tool making, mould making and model making

- Blow moulds, injection moulds and vacuum moulds - Laminating tools Pressing technique

- Anvil cap and stamp holder Base plates, table tops and mounting plates

Areas of application

- Structures with high strength requirements

Features of this material

  • Rolled plates: according to thickness stretched or compressed
  • Optimised for high core strength and optimal dimensional stability for higher strengths
  • Very good machinability

Information about the material

  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)
  • Aviation
    Aviation No
  • Chemical specifications
    Cr (to) 0.05
    Cu (from) 1.5
    Cu (to) 2.6
    Fe (to) 0.35
    Mg (from) 1.8
    Mg (to) 2.6
    Mn (to) 0.1
    Other 0,05
    Rest Aluminium
    Si (to) 0.3
    Ti (to) 0.06
    Total 0,15
    Zn (from) 5.7
    Zn (to) 7.6
    Zr (from) 0.08
    Zr (to) 0.25
  • Chemical surface treatment
    Anodise - decorative 3
    Anodising - protective anodising 2
  • Corrosion resistance
    Normal atmosphere 3
    Seawater atmosphere 3
  • Food industry
    suitable according to DIN EN 602 No
  • Forming
    Bending 5
    Deep drawing (conditional) 5
    Drop forging 5
    Extruding 5
    Impact extrusion 5
    Open die forging 5
    Press 5
    Upsetting (Conditional) 5
  • Machining / Machinability
    dimensional stability 3
    Eroding 1
    hardened 1
  • Material
    Material chemically EN 573-3 7,050
    DIN -
    DIN (old designation) Al Zn6 Cu Mg Zr
    France AFNOR -
    Italy UNI -
    Norway -
    Spain -
    Sweden -
    United Kingdom BS -
  • Mechanical surface treatment
    Polishing 1
  • physical properties
    Coefficient of thermal expansion from 20 to 100°C 23.5 K⁻¹10⁻⁶
    Density 2.83 g/cm³
    Electrical conductivity min. 23 m/Ω*mm²
    Modulus of elasticity 70.3 GPa
    Thermal conductivity min. 154 W/m*K
  • Welding
    MIG 3
    Resistance spot welding 3
    TIG 3
    welding additives
    • S Al Si5 (4043)
    • S Al Mg4,5 Mn (5183)
    • S Al Mg5 Mn (5556)
    • S Al Cu6 Mn Zr Ti (2319)

1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified