FORMODAL® 036 high-strength
cast plate - all sides sawn
- Form cast plate - all sides sawn
- Material Aluminum
- Material FORMODAL® 036 high-strength
- Material chemically EN 573-3 FORMODAL 036-Guss nach Art 7021
- DIN -
| Aviation | No |
| Anodise - decorative | 5 |
| Anodising - protective anodising | 2 |
| Chromating | 2 |
| Cleaning / degreasing | 2 |
| Hard anodising | 2 |
| Phosphating | 2 |
| Pickling | 2 |
| Shining | 4.5 |
| Normal atmosphere | 2 |
| Seawater atmosphere | 4 |
| Laser cutting | 3 |
| Plasma cutting | 2 |
| Sawing | 1 |
| Shear cutting | 2 |
| Waterjet cutting | 1 |
| suitable according to DIN EN 602 | No |
| dimensional stability | 1 |
| Eroding | 1 |
| Etching | 2 |
| hardened | 1 |
| Photo etching | 4 |
| Material chemically EN 573-3 | FORMODAL 036-Guss nach Art 7021 |
| DIN | - |
| DIN (old designation) | - |
| France AFNOR | - |
| Italy UNI | - |
| Norway | - |
| Spain | - |
| Sweden | - |
| United Kingdom BS | - |
| Blasting | 1 |
| Brushing | 2 |
| Grinding | 2 |
| Galvanising | 2 |
| Nickel coating | 2 |
| Thermal spraying | 4 |
| Enamelling | 5 |
| Laminating | 2 |
| Coefficient of thermal expansion from 20 to 100°C (typical) | 23.7 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 200°C (typical) | 23.7 K⁻¹10⁻⁶ |
| Coefficient of thermal expansion from 20 to 300°C (typical) | 23.7 K⁻¹10⁻⁶ |
| Density (typical) | 2.78 g/cm³ |
| Electrical conductivity max. (typical) | 23 m/Ω*mm² |
| Electrical conductivity min. (typical) | 19 m/Ω*mm² |
| Modulus of elasticity (typical) | 72 GPa |
| Thermal conductivity min. (typical) | 150 W/m*K |
| Friction stir welding | 2 |
| Friction welding | 2 |
| Gas | 5 |
| Laser | 2 |
| MIG | 5 |
| Plasma | 2 |
| Resistance spot welding | 1 |
| TIG | 2 |
| welding additives |
|
1 very good
2 good
3 moderate
4 poor
5 unsuited
0 Not specified